SAE-AISI H22 Steel vs. SAE-AISI M34 Steel
Both SAE-AISI H22 steel and SAE-AISI M34 steel are iron alloys. They have 80% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI H22 steel and the bottom bar is SAE-AISI M34 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 1920 | |
| 800 to 2170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Melting Completion (Liquidus), °C | 1670 | |
| 1540 |
| Melting Onset (Solidus), °C | 1620 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Conductivity, W/m-K | 31 | |
| 24 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 32 |
| Density, g/cm3 | 8.7 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 9.5 |
| Embodied Energy, MJ/kg | 73 | |
| 140 |
| Embodied Water, L/kg | 72 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 21 | |
| 35 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 61 | |
| 27 to 74 |
| Strength to Weight: Bending, points | 20 to 39 | |
| 23 to 46 |
| Thermal Diffusivity, mm2/s | 8.2 | |
| 6.7 |
| Thermal Shock Resistance, points | 22 to 60 | |
| 25 to 67 |
Alloy Composition
| Carbon (C), % | 0.3 to 0.4 | |
| 0.85 to 0.92 |
| Chromium (Cr), % | 1.8 to 3.8 | |
| 3.5 to 4.0 |
| Cobalt (Co), % | 0 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 82.2 to 87.4 | |
| 71.3 to 76.5 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 7.8 to 9.2 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0.2 to 0.45 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 10 to 11.8 | |
| 1.4 to 2.1 |
| Vanadium (V), % | 0.25 to 0.5 | |
| 1.9 to 2.3 |