SAE-AISI H43 Steel vs. AISI 410Cb Stainless Steel

Both SAE-AISI H43 steel and AISI 410Cb stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is AISI 410Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 710 to 2140
550 to 960

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Melting Completion (Liquidus), °C 1530
1450
Melting Onset (Solidus), °C 1480
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 30
27
Thermal Expansion, µm/m-K 12
10

Otherwise Unclassified Properties

Base Metal Price, % relative 14
7.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 8.2
2.0
Embodied Energy, MJ/kg 120
29
Embodied Water, L/kg 100
97

Common Calculations

PREN (Pitting Resistance) 31
12
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 75
20 to 35
Strength to Weight: Bending, points 22 to 46
19 to 28
Thermal Diffusivity, mm2/s 8.3
7.3
Thermal Shock Resistance, points 21 to 62
20 to 35

Alloy Composition

Carbon (C), % 0.5 to 0.65
0 to 0.18
Chromium (Cr), % 3.8 to 4.5
11 to 13
Iron (Fe), % 83.2 to 85.9
84.5 to 89
Manganese (Mn), % 0.15 to 0.4
0 to 1.0
Molybdenum (Mo), % 7.8 to 8.5
0
Niobium (Nb), % 0
0.050 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 1.8 to 2.2
0

Comparable Variants