SAE-AISI H43 Steel vs. EN 1.4422 Stainless Steel

Both SAE-AISI H43 steel and EN 1.4422 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is EN 1.4422 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 710 to 2140
850

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Melting Completion (Liquidus), °C 1530
1450
Melting Onset (Solidus), °C 1480
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 30
16
Thermal Expansion, µm/m-K 12
10

Otherwise Unclassified Properties

Base Metal Price, % relative 14
11
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 8.2
2.7
Embodied Energy, MJ/kg 120
37
Embodied Water, L/kg 100
110

Common Calculations

PREN (Pitting Resistance) 31
17
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 75
30
Strength to Weight: Bending, points 22 to 46
25
Thermal Diffusivity, mm2/s 8.3
4.3
Thermal Shock Resistance, points 21 to 62
31

Alloy Composition

Carbon (C), % 0.5 to 0.65
0 to 0.020
Chromium (Cr), % 3.8 to 4.5
11 to 13
Copper (Cu), % 0
0.2 to 0.8
Iron (Fe), % 83.2 to 85.9
76.8 to 83.5
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 7.8 to 8.5
1.3 to 1.8
Nickel (Ni), % 0
4.0 to 5.0
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.45
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0030
Vanadium (V), % 1.8 to 2.2
0