MakeItFrom.com
Menu (ESC)

SAE-AISI H43 Steel vs. EN 1.4864 Stainless Steel

Both SAE-AISI H43 steel and EN 1.4864 stainless steel are iron alloys. They have 51% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is EN 1.4864 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 710 to 2140
650

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Melting Completion (Liquidus), °C 1530
1390
Melting Onset (Solidus), °C 1480
1340
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 30
13
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 14
30
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 8.2
5.3
Embodied Energy, MJ/kg 120
75
Embodied Water, L/kg 100
180

Common Calculations

PREN (Pitting Resistance) 31
17
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 75
23
Strength to Weight: Bending, points 22 to 46
21
Thermal Diffusivity, mm2/s 8.3
3.3
Thermal Shock Resistance, points 21 to 62
17

Alloy Composition

Carbon (C), % 0.5 to 0.65
0 to 0.15
Chromium (Cr), % 3.8 to 4.5
15 to 17
Iron (Fe), % 83.2 to 85.9
41.7 to 51
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 7.8 to 8.5
0
Nickel (Ni), % 0
33 to 37
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.2 to 0.45
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 1.8 to 2.2
0