SAE-AISI H43 Steel vs. SAE-AISI M3 Class 1 Steel

Both SAE-AISI H43 steel and SAE-AISI M3 class 1 steel are iron alloys. They have a moderately high 93% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is SAE-AISI M3 class 1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 710 to 2140
770 to 2150

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Melting Completion (Liquidus), °C 1530
1610
Melting Onset (Solidus), °C 1480
1570
Specific Heat Capacity, J/kg-K 460
440
Thermal Conductivity, W/m-K 30
26
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 14
25
Density, g/cm3 7.9
8.3
Embodied Carbon, kg CO2/kg material 8.2
10
Embodied Energy, MJ/kg 120
150
Embodied Water, L/kg 100
100

Common Calculations

PREN (Pitting Resistance) 31
33
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 25 to 75
26 to 72
Strength to Weight: Bending, points 22 to 46
22 to 44
Thermal Diffusivity, mm2/s 8.3
7.2
Thermal Shock Resistance, points 21 to 62
24 to 67

Alloy Composition

Carbon (C), % 0.5 to 0.65
1.0 to 1.1
Chromium (Cr), % 3.8 to 4.5
3.8 to 4.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 83.2 to 85.9
76.9 to 82.9
Manganese (Mn), % 0.15 to 0.4
0.15 to 0.4
Molybdenum (Mo), % 7.8 to 8.5
4.8 to 6.5
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 0.45
0.2 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
5.0 to 6.8
Vanadium (V), % 1.8 to 2.2
2.3 to 2.8