SAE-AISI H43 Steel vs. SAE-AISI M30 Steel

Both SAE-AISI H43 steel and SAE-AISI M30 steel are iron alloys. They have a moderately high 93% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is SAE-AISI M30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 710 to 2140
800 to 2170

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Melting Completion (Liquidus), °C 1530
1550
Melting Onset (Solidus), °C 1480
1500
Specific Heat Capacity, J/kg-K 460
450
Thermal Conductivity, W/m-K 30
24
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 14
26
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 8.2
7.2
Embodied Energy, MJ/kg 120
100
Embodied Water, L/kg 100
120

Common Calculations

PREN (Pitting Resistance) 31
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 75
27 to 74
Strength to Weight: Bending, points 22 to 46
24 to 46
Thermal Diffusivity, mm2/s 8.3
6.6
Thermal Shock Resistance, points 21 to 62
25 to 67

Alloy Composition

Carbon (C), % 0.5 to 0.65
0.75 to 0.85
Chromium (Cr), % 3.8 to 4.5
3.5 to 4.3
Cobalt (Co), % 0
4.5 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 83.2 to 85.9
75.2 to 80.9
Manganese (Mn), % 0.15 to 0.4
0.15 to 0.4
Molybdenum (Mo), % 7.8 to 8.5
7.8 to 9.0
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 0.45
0.2 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
1.3 to 2.3
Vanadium (V), % 1.8 to 2.2
1.0 to 1.4

Comparable Variants