SAE-AISI H43 Steel vs. C79200 Nickel Silver
SAE-AISI H43 steel belongs to the iron alloys classification, while C79200 nickel silver belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is C79200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 2140 | |
| 480 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 190 |
| Melting Completion (Liquidus), °C | 1530 | |
| 950 |
| Melting Onset (Solidus), °C | 1480 | |
| 910 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 390 |
| Thermal Conductivity, W/m-K | 30 | |
| 42 |
| Thermal Expansion, µm/m-K | 12 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 30 |
| Density, g/cm3 | 7.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 3.6 |
| Embodied Energy, MJ/kg | 120 | |
| 56 |
| Embodied Water, L/kg | 100 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 25 to 75 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 22 to 46 | |
| 16 to 18 |
| Thermal Diffusivity, mm2/s | 8.3 | |
| 13 |
| Thermal Shock Resistance, points | 21 to 62 | |
| 16 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.5 to 0.65 | |
| 0 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 59 to 66.5 |
| Iron (Fe), % | 83.2 to 85.9 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0.8 to 1.4 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 7.8 to 8.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 11 to 13 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.45 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 1.8 to 2.2 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 17.9 to 29.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |