SAE-AISI H43 Steel vs. N06230 Nickel
SAE-AISI H43 steel belongs to the iron alloys classification, while N06230 nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is N06230 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 2140 | |
| 620 to 840 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 310 |
| Melting Completion (Liquidus), °C | 1530 | |
| 1370 |
| Melting Onset (Solidus), °C | 1480 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 420 |
| Thermal Conductivity, W/m-K | 30 | |
| 8.9 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 85 |
| Density, g/cm3 | 7.9 | |
| 9.5 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 11 |
| Embodied Energy, MJ/kg | 120 | |
| 160 |
| Embodied Water, L/kg | 100 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 12 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 25 to 75 | |
| 18 to 25 |
| Strength to Weight: Bending, points | 22 to 46 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 8.3 | |
| 2.3 |
| Thermal Shock Resistance, points | 21 to 62 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.2 to 0.5 |
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0.5 to 0.65 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 20 to 24 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Iron (Fe), % | 83.2 to 85.9 | |
| 0 to 3.0 |
| Lanthanum (La), % | 0 | |
| 0.0050 to 0.050 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.3 to 1.0 |
| Molybdenum (Mo), % | 7.8 to 8.5 | |
| 1.0 to 3.0 |
| Nickel (Ni), % | 0 | |
| 47.5 to 65.2 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.45 | |
| 0.25 to 0.75 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 13 to 15 |
| Vanadium (V), % | 1.8 to 2.2 | |
| 0 |