Both SAE-AISI H43 steel and S30435 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H43 steel and the bottom bar is S30435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 710 to 2140
510

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Melting Completion (Liquidus), °C 1530
1420
Melting Onset (Solidus), °C 1480
1380
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 30
16
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 14
14
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 8.2
2.9
Embodied Energy, MJ/kg 120
40
Embodied Water, L/kg 100
140

Common Calculations

PREN (Pitting Resistance) 31
17
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 75
18
Strength to Weight: Bending, points 22 to 46
18
Thermal Diffusivity, mm2/s 8.3
4.2
Thermal Shock Resistance, points 21 to 62
12

Alloy Composition

Carbon (C), % 0.5 to 0.65
0 to 0.080
Chromium (Cr), % 3.8 to 4.5
16 to 18
Copper (Cu), % 0
1.5 to 3.0
Iron (Fe), % 83.2 to 85.9
66.9 to 75.5
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 7.8 to 8.5
0
Nickel (Ni), % 0
7.0 to 9.0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.2 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 1.8 to 2.2
0