SAE-AISI L3 Steel vs. EN 1.7006 Steel

Both SAE-AISI L3 steel and EN 1.7006 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI L3 steel and the bottom bar is EN 1.7006 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 600 to 2250
530 to 1890

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.4
Embodied Energy, MJ/kg 27
19
Embodied Water, L/kg 53
48

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 80
19 to 67
Strength to Weight: Bending, points 20 to 49
19 to 43
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 18 to 67
16 to 56

Alloy Composition

Carbon (C), % 1.0 to 1.1
0.42 to 0.5
Chromium (Cr), % 1.3 to 1.7
0.4 to 0.6
Iron (Fe), % 95.5 to 97.3
97.6 to 98.7
Manganese (Mn), % 0.25 to 0.8
0.5 to 0.8
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.1 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035
Vanadium (V), % 0.1 to 0.3
0

Comparable Variants