SAE-AISI M2 Steel vs. EN 1.7379 Steel

Both SAE-AISI M2 steel and EN 1.7379 steel are iron alloys. They have 85% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M2 steel and the bottom bar is EN 1.7379 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 760 to 2150
670

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Melting Completion (Liquidus), °C 1610
1470
Melting Onset (Solidus), °C 1570
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 22
39
Thermal Expansion, µm/m-K 10
13

Otherwise Unclassified Properties

Base Metal Price, % relative 24
3.8
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.8
1.8
Embodied Energy, MJ/kg 130
23
Embodied Water, L/kg 98
59

Common Calculations

PREN (Pitting Resistance) 31
5.7
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 25 to 71
24
Strength to Weight: Bending, points 22 to 44
22
Thermal Diffusivity, mm2/s 5.9
11
Thermal Shock Resistance, points 27 to 76
19

Alloy Composition

Carbon (C), % 0.78 to 1.1
0.13 to 0.2
Chromium (Cr), % 3.8 to 4.5
2.0 to 2.5
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 78.5 to 83.4
94.5 to 96.5
Manganese (Mn), % 0.15 to 0.4
0.5 to 0.9
Molybdenum (Mo), % 4.5 to 5.5
0.9 to 1.2
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.2 to 0.45
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 5.5 to 6.8
0
Vanadium (V), % 1.8 to 2.2
0