SAE-AISI M2 Steel vs. CC498K Bronze

SAE-AISI M2 steel belongs to the iron alloys classification, while CC498K bronze belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M2 steel and the bottom bar is CC498K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 77
41
Tensile Strength: Ultimate (UTS), MPa 760 to 2150
260

Thermal Properties

Latent Heat of Fusion, J/g 260
190
Melting Completion (Liquidus), °C 1610
1000
Melting Onset (Solidus), °C 1570
920
Specific Heat Capacity, J/kg-K 440
370
Thermal Conductivity, W/m-K 22
73
Thermal Expansion, µm/m-K 10
18

Otherwise Unclassified Properties

Base Metal Price, % relative 24
32
Density, g/cm3 8.4
8.8
Embodied Carbon, kg CO2/kg material 8.8
3.2
Embodied Energy, MJ/kg 130
52
Embodied Water, L/kg 98
360

Common Calculations

Stiffness to Weight: Axial, points 13
6.9
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 25 to 71
8.1
Strength to Weight: Bending, points 22 to 44
10
Thermal Diffusivity, mm2/s 5.9
22
Thermal Shock Resistance, points 27 to 76
9.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0.78 to 1.1
0
Chromium (Cr), % 3.8 to 4.5
0
Copper (Cu), % 0 to 0.25
85 to 90
Iron (Fe), % 78.5 to 83.4
0 to 0.25
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0.15 to 0.4
0
Molybdenum (Mo), % 4.5 to 5.5
0
Nickel (Ni), % 0 to 0.3
0 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.050
Silicon (Si), % 0.2 to 0.45
0 to 0.010
Sulfur (S), % 0 to 0.030
0 to 0.1
Tin (Sn), % 0
5.5 to 6.5
Tungsten (W), % 5.5 to 6.8
0
Vanadium (V), % 1.8 to 2.2
0
Zinc (Zn), % 0
3.0 to 5.0