SAE-AISI M2 Steel vs. SAE-AISI M30 Steel

Both SAE-AISI M2 steel and SAE-AISI M30 steel are iron alloys. They have a moderately high 92% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI M2 steel and the bottom bar is SAE-AISI M30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 760 to 2150
800 to 2170

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1610
1550
Melting Onset (Solidus), °C 1570
1500
Specific Heat Capacity, J/kg-K 440
450
Thermal Conductivity, W/m-K 22
24
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 24
26
Density, g/cm3 8.4
8.2
Embodied Carbon, kg CO2/kg material 8.8
7.2
Embodied Energy, MJ/kg 130
100
Embodied Water, L/kg 98
120

Common Calculations

PREN (Pitting Resistance) 31
35
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 25 to 71
27 to 74
Strength to Weight: Bending, points 22 to 44
24 to 46
Thermal Diffusivity, mm2/s 5.9
6.6
Thermal Shock Resistance, points 27 to 76
25 to 67

Alloy Composition

Carbon (C), % 0.78 to 1.1
0.75 to 0.85
Chromium (Cr), % 3.8 to 4.5
3.5 to 4.3
Cobalt (Co), % 0
4.5 to 5.5
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 78.5 to 83.4
75.2 to 80.9
Manganese (Mn), % 0.15 to 0.4
0.15 to 0.4
Molybdenum (Mo), % 4.5 to 5.5
7.8 to 9.0
Nickel (Ni), % 0 to 0.3
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 0.45
0.2 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 5.5 to 6.8
1.3 to 2.3
Vanadium (V), % 1.8 to 2.2
1.0 to 1.4