SAE-AISI M3 Class 1 Steel vs. R30075 Cobalt

SAE-AISI M3 class 1 steel belongs to the iron alloys classification, while R30075 cobalt belongs to the cobalt alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M3 class 1 steel and the bottom bar is R30075 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210 to 250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
82 to 98
Tensile Strength: Ultimate (UTS), MPa 770 to 2150
780 to 1280

Thermal Properties

Latent Heat of Fusion, J/g 260
320
Melting Completion (Liquidus), °C 1610
1360
Melting Onset (Solidus), °C 1570
1290
Specific Heat Capacity, J/kg-K 440
450
Thermal Conductivity, W/m-K 26
13
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Density, g/cm3 8.3
8.4
Embodied Carbon, kg CO2/kg material 10
8.1
Embodied Energy, MJ/kg 150
110
Embodied Water, L/kg 100
530

Common Calculations

Stiffness to Weight: Axial, points 13
14 to 17
Stiffness to Weight: Bending, points 23
24 to 25
Strength to Weight: Axial, points 26 to 72
26 to 42
Strength to Weight: Bending, points 22 to 44
22 to 31
Thermal Diffusivity, mm2/s 7.2
3.5
Thermal Shock Resistance, points 24 to 67
21 to 29

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Boron (B), % 0
0 to 0.010
Carbon (C), % 1.0 to 1.1
0 to 0.35
Chromium (Cr), % 3.8 to 4.5
27 to 30
Cobalt (Co), % 0
58.7 to 68
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 76.9 to 82.9
0 to 0.75
Manganese (Mn), % 0.15 to 0.4
0 to 1.0
Molybdenum (Mo), % 4.8 to 6.5
5.0 to 7.0
Nickel (Ni), % 0 to 0.3
0 to 0.5
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0.2 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.1
Tungsten (W), % 5.0 to 6.8
0 to 0.2
Vanadium (V), % 2.3 to 2.8
0

Comparable Variants