SAE-AISI M3 Class 2 Steel vs. ACI-ASTM CF8 Steel

Both SAE-AISI M3 class 2 steel and ACI-ASTM CF8 steel are iron alloys. They have 74% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M3 class 2 steel and the bottom bar is ACI-ASTM CF8 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 770 to 2210
540

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Melting Completion (Liquidus), °C 1620
1420
Melting Onset (Solidus), °C 1570
1430
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 26
16
Thermal Expansion, µm/m-K 12
15

Otherwise Unclassified Properties

Base Metal Price, % relative 25
16
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 12
3.1
Embodied Energy, MJ/kg 180
44
Embodied Water, L/kg 110
150

Common Calculations

PREN (Pitting Resistance) 33
20
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 26 to 74
19
Strength to Weight: Bending, points 22 to 45
19
Thermal Diffusivity, mm2/s 7.2
4.3
Thermal Shock Resistance, points 24 to 69
13

Alloy Composition

Carbon (C), % 1.2 to 1.3
0 to 0.080
Chromium (Cr), % 3.8 to 4.5
18 to 21
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 75.8 to 82.3
63.8 to 74
Manganese (Mn), % 0.15 to 0.4
0 to 1.5
Molybdenum (Mo), % 4.8 to 6.5
0 to 0.5
Nickel (Ni), % 0 to 0.3
8.0 to 11
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.45
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040
Tungsten (W), % 5.0 to 6.8
0
Vanadium (V), % 2.8 to 3.8
0