SAE-AISI M3 Class 2 Steel vs. EN 1.4911 Stainless Steel

Both SAE-AISI M3 class 2 steel and EN 1.4911 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M3 class 2 steel and the bottom bar is EN 1.4911 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 770 to 2210
1070

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1620
1450
Melting Onset (Solidus), °C 1570
1410
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 26
20
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 25
20
Density, g/cm3 8.3
7.9
Embodied Carbon, kg CO2/kg material 12
3.4
Embodied Energy, MJ/kg 180
49
Embodied Water, L/kg 110
130

Common Calculations

PREN (Pitting Resistance) 33
14
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 26 to 74
38
Strength to Weight: Bending, points 22 to 45
30
Thermal Diffusivity, mm2/s 7.2
5.4
Thermal Shock Resistance, points 24 to 69
37

Alloy Composition

Boron (B), % 0
0.0050 to 0.015
Carbon (C), % 1.2 to 1.3
0.050 to 0.12
Chromium (Cr), % 3.8 to 4.5
9.8 to 11.2
Cobalt (Co), % 0
5.0 to 7.0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 75.8 to 82.3
75.7 to 83.8
Manganese (Mn), % 0.15 to 0.4
0.3 to 1.3
Molybdenum (Mo), % 4.8 to 6.5
0.5 to 1.0
Nickel (Ni), % 0 to 0.3
0.2 to 1.2
Niobium (Nb), % 0
0.2 to 0.5
Nitrogen (N), % 0
0 to 0.035
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.2 to 0.45
0.1 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 5.0 to 6.8
0 to 0.7
Vanadium (V), % 2.8 to 3.8
0.1 to 0.4