SAE-AISI M42 Steel vs. ASTM Grade HP Steel

Both SAE-AISI M42 steel and ASTM grade HP steel are iron alloys. They have 42% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M42 steel and the bottom bar is ASTM grade HP steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 810 to 2310
490

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Melting Completion (Liquidus), °C 1540
1370
Melting Onset (Solidus), °C 1490
1330
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 20
12
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 30
34
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 7.4
5.8
Embodied Energy, MJ/kg 100
82
Embodied Water, L/kg 140
220

Common Calculations

PREN (Pitting Resistance) 38
27
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 28 to 79
17
Strength to Weight: Bending, points 24 to 48
17
Thermal Diffusivity, mm2/s 5.4
3.2
Thermal Shock Resistance, points 25 to 71
11

Alloy Composition

Carbon (C), % 1.1 to 1.2
0.35 to 0.75
Chromium (Cr), % 3.5 to 4.3
24 to 28
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 76.3 to 81
29.2 to 42.7
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 9.0 to 10
0 to 0.5
Nickel (Ni), % 0 to 0.3
33 to 37
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.15 to 0.65
0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.040
Tungsten (W), % 1.2 to 1.9
0
Vanadium (V), % 1.0 to 1.4
0