SAE-AISI M42 Steel vs. EN 1.4460 Stainless Steel

Both SAE-AISI M42 steel and EN 1.4460 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M42 steel and the bottom bar is EN 1.4460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 810 to 2310
750

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Melting Completion (Liquidus), °C 1540
1430
Melting Onset (Solidus), °C 1490
1390
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 20
15
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 30
18
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 7.4
3.4
Embodied Energy, MJ/kg 100
48
Embodied Water, L/kg 140
180

Common Calculations

PREN (Pitting Resistance) 38
34
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 28 to 79
27
Strength to Weight: Bending, points 24 to 48
24
Thermal Diffusivity, mm2/s 5.4
4.0
Thermal Shock Resistance, points 25 to 71
20

Alloy Composition

Carbon (C), % 1.1 to 1.2
0 to 0.050
Chromium (Cr), % 3.5 to 4.3
25 to 28
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 76.3 to 81
60.2 to 69.2
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 9.0 to 10
1.3 to 2.0
Nickel (Ni), % 0 to 0.3
4.5 to 6.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.15 to 0.65
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 1.2 to 1.9
0
Vanadium (V), % 1.0 to 1.4
0