SAE-AISI M43 Steel vs. Grade 29 Titanium
SAE-AISI M43 steel belongs to the iron alloys classification, while grade 29 titanium belongs to the titanium alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M43 steel and the bottom bar is grade 29 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 2290 | |
| 930 to 940 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 410 |
| Melting Completion (Liquidus), °C | 1550 | |
| 1610 |
| Melting Onset (Solidus), °C | 1500 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 560 |
| Thermal Conductivity, W/m-K | 19 | |
| 7.3 |
| Thermal Expansion, µm/m-K | 12 | |
| 9.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 36 |
| Density, g/cm3 | 8.2 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 39 |
| Embodied Energy, MJ/kg | 120 | |
| 640 |
| Embodied Water, L/kg | 140 | |
| 410 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 27 to 77 | |
| 58 to 59 |
| Strength to Weight: Bending, points | 24 to 47 | |
| 47 to 48 |
| Thermal Diffusivity, mm2/s | 5.3 | |
| 2.9 |
| Thermal Shock Resistance, points | 25 to 71 | |
| 68 to 69 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 5.5 to 6.5 |
| Carbon (C), % | 1.2 to 1.3 | |
| 0 to 0.080 |
| Chromium (Cr), % | 3.5 to 4.3 | |
| 0 |
| Cobalt (Co), % | 7.8 to 8.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 70.8 to 76 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 7.5 to 8.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.13 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Ruthenium (Ru), % | 0 | |
| 0.080 to 0.14 |
| Silicon (Si), % | 0.15 to 0.65 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 88 to 90.9 |
| Tungsten (W), % | 2.3 to 3.0 | |
| 0 |
| Vanadium (V), % | 1.5 to 1.8 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |