SAE-AISI M46 Steel vs. AWS E330
Both SAE-AISI M46 steel and AWS E330 are iron alloys. They have 52% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M46 steel and the bottom bar is AWS E330.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 2300 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1400 |
| Melting Onset (Solidus), °C | 1500 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 18 | |
| 12 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 31 |
| Density, g/cm3 | 8.1 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 5.4 |
| Embodied Energy, MJ/kg | 180 | |
| 75 |
| Embodied Water, L/kg | 150 | |
| 180 |
Common Calculations
| PREN (Pitting Resistance) | 35 | |
| 17 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 27 to 78 | |
| 20 |
| Strength to Weight: Bending, points | 24 to 48 | |
| 19 |
| Thermal Diffusivity, mm2/s | 4.9 | |
| 3.2 |
| Thermal Shock Resistance, points | 25 to 71 | |
| 16 |
Alloy Composition
| Carbon (C), % | 1.2 to 1.3 | |
| 0.18 to 0.25 |
| Chromium (Cr), % | 3.7 to 4.2 | |
| 14 to 17 |
| Cobalt (Co), % | 7.8 to 8.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.75 |
| Iron (Fe), % | 70 to 73.8 | |
| 40.7 to 51.8 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 1.0 to 2.5 |
| Molybdenum (Mo), % | 8.0 to 8.5 | |
| 0 to 0.75 |
| Nickel (Ni), % | 0 to 0.3 | |
| 33 to 37 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.4 to 0.65 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 1.9 to 2.2 | |
| 0 |
| Vanadium (V), % | 3.0 to 3.3 | |
| 0 |