SAE-AISI M52 Steel vs. EN 1.4886 Stainless Steel

Both SAE-AISI M52 steel and EN 1.4886 stainless steel are iron alloys. They have 49% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M52 steel and the bottom bar is EN 1.4886 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
76
Tensile Strength: Ultimate (UTS), MPa 710 to 2280
580

Thermal Properties

Latent Heat of Fusion, J/g 260
320
Melting Completion (Liquidus), °C 1510
1390
Melting Onset (Solidus), °C 1470
1340
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 31
12
Thermal Expansion, µm/m-K 13
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 10
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 7.5
5.4
Embodied Energy, MJ/kg 110
76
Embodied Water, L/kg 89
190

Common Calculations

PREN (Pitting Resistance) 20
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 80
20
Strength to Weight: Bending, points 22 to 49
19
Thermal Diffusivity, mm2/s 8.4
3.1
Thermal Shock Resistance, points 21 to 67
14

Alloy Composition

Carbon (C), % 0.85 to 1.0
0 to 0.15
Chromium (Cr), % 3.5 to 4.3
17 to 20
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 84.4 to 88.9
38.7 to 49
Manganese (Mn), % 0.15 to 0.45
0 to 2.0
Molybdenum (Mo), % 4.0 to 4.9
0
Nickel (Ni), % 0 to 0.3
33 to 37
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 0.6
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0.75 to 1.5
0
Vanadium (V), % 1.7 to 2.3
0