SAE-AISI M52 Steel vs. SAE-AISI S6 Steel

Both SAE-AISI M52 steel and SAE-AISI S6 steel are iron alloys. They have a moderately high 90% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI M52 steel and the bottom bar is SAE-AISI S6 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
72
Tensile Strength: Ultimate (UTS), MPa 710 to 2280
670 to 1920

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1510
1430
Melting Onset (Solidus), °C 1470
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 31
41
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
3.2
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 7.5
2.3
Embodied Energy, MJ/kg 110
33
Embodied Water, L/kg 89
56

Common Calculations

PREN (Pitting Resistance) 20
2.7
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 80
24 to 70
Strength to Weight: Bending, points 22 to 49
22 to 45
Thermal Diffusivity, mm2/s 8.4
11
Thermal Shock Resistance, points 21 to 67
22 to 64

Alloy Composition

Carbon (C), % 0.85 to 1.0
0.4 to 0.5
Chromium (Cr), % 3.5 to 4.3
1.2 to 1.5
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 84.4 to 88.9
92.8 to 94.7
Manganese (Mn), % 0.15 to 0.45
1.2 to 1.5
Molybdenum (Mo), % 4.0 to 4.9
0.3 to 0.5
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 0.6
2.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.75 to 1.5
0
Vanadium (V), % 1.7 to 2.3
0.2 to 0.4

Comparable Variants