SAE-AISI M6 Steel vs. Solder Alloy 151
SAE-AISI M6 steel belongs to the iron alloys classification, while solder alloy 151 belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M6 steel and the bottom bar is solder alloy 151.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 39 |
| Poisson's Ratio | 0.29 | |
| 0.37 |
| Shear Modulus, GPa | 77 | |
| 14 |
| Tensile Strength: Ultimate (UTS), MPa | 840 to 2210 | |
| 46 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 47 |
| Melting Completion (Liquidus), °C | 1560 | |
| 150 |
| Melting Onset (Solidus), °C | 1510 | |
| 150 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 190 |
| Thermal Conductivity, W/m-K | 17 | |
| 44 |
| Thermal Expansion, µm/m-K | 12 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 9.2 |
| Embodied Energy, MJ/kg | 120 | |
| 160 |
| Embodied Water, L/kg | 160 | |
| 920 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 2.5 |
| Stiffness to Weight: Bending, points | 23 | |
| 13 |
| Strength to Weight: Axial, points | 28 to 73 | |
| 1.4 |
| Strength to Weight: Bending, points | 24 to 45 | |
| 3.2 |
| Thermal Diffusivity, mm2/s | 4.7 | |
| 26 |
| Thermal Shock Resistance, points | 26 to 68 | |
| 3.2 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 17.5 to 18.5 |
| Carbon (C), % | 0.75 to 0.85 | |
| 0 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 0 |
| Cobalt (Co), % | 11 to 13 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 68.8 to 74.6 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 30.3 to 33 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 4.5 to 5.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.45 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 49.5 to 50.5 |
| Tungsten (W), % | 3.8 to 4.8 | |
| 0 |
| Vanadium (V), % | 1.3 to 1.7 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |