SAE-AISI M62 Steel vs. K94200 Alloy
Both SAE-AISI M62 steel and K94200 alloy are iron alloys. There are 13 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M62 steel and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 140 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 79 | |
| 54 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 2440 | |
| 500 to 710 |
Thermal Properties
| Melting Onset (Solidus), °C | 1600 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 500 |
| Thermal Expansion, µm/m-K | 12 | |
| 5.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 27 to 80 | |
| 17 to 24 |
| Strength to Weight: Bending, points | 23 to 47 | |
| 17 to 22 |
| Thermal Shock Resistance, points | 24 to 71 | |
| 49 to 70 |