SAE-AISI O7 Steel vs. EN 1.4571 Stainless Steel
Both SAE-AISI O7 steel and EN 1.4571 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI O7 steel and the bottom bar is EN 1.4571 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 2110 | |
| 600 to 900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1440 |
| Melting Onset (Solidus), °C | 1430 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 41 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.0 | |
| 19 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 3.9 |
| Embodied Energy, MJ/kg | 33 | |
| 54 |
| Embodied Water, L/kg | 52 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 3.6 | |
| 25 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 24 to 74 | |
| 21 to 32 |
| Strength to Weight: Bending, points | 22 to 46 | |
| 20 to 26 |
| Thermal Diffusivity, mm2/s | 11 | |
| 4.0 |
| Thermal Shock Resistance, points | 23 to 70 | |
| 13 to 20 |
Alloy Composition
| Carbon (C), % | 1.1 to 1.3 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0.35 to 0.85 | |
| 16.5 to 18.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 92.9 to 97.6 | |
| 61.7 to 71 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 2.0 to 2.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 10.5 to 13.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0 to 0.7 |
| Tungsten (W), % | 1.0 to 2.0 | |
| 0 |
| Vanadium (V), % | 0 to 0.4 | |
| 0 |