SAE-AISI T1 Steel vs. ASTM B628 Ag-Cu
SAE-AISI T1 steel belongs to the iron alloys classification, while ASTM B628 Ag-Cu belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI T1 steel and the bottom bar is ASTM B628 Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 83 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 80 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 2130 | |
| 350 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 140 |
| Melting Completion (Liquidus), °C | 1810 | |
| 780 |
| Melting Onset (Solidus), °C | 1750 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 280 |
| Thermal Expansion, µm/m-K | 12 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 4.6 |
| Stiffness to Weight: Bending, points | 21 | |
| 14 |
| Strength to Weight: Axial, points | 23 to 64 | |
| 9.5 to 21 |
| Strength to Weight: Bending, points | 20 to 40 | |
| 11 to 18 |
| Thermal Shock Resistance, points | 23 to 64 | |
| 16 to 34 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0.65 to 0.8 | |
| 0 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 26.6 to 29 |
| Iron (Fe), % | 73.2 to 77.2 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0.1 to 0.4 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0 |
| Silver (Ag), % | 0 | |
| 71 to 73 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 17.3 to 18.8 | |
| 0 |
| Vanadium (V), % | 0.9 to 1.3 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.060 |
| Residuals, % | 0 | |
| 0 to 0.21 |