SAE-AISI T5 Steel vs. N06255 Nickel
SAE-AISI T5 steel belongs to the iron alloys classification, while N06255 nickel belongs to the nickel alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI T5 steel and the bottom bar is N06255 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 860 to 2140 | |
| 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Melting Completion (Liquidus), °C | 1810 | |
| 1470 |
| Melting Onset (Solidus), °C | 1750 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 450 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 55 |
| Density, g/cm3 | 9.4 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 9.4 |
| Embodied Energy, MJ/kg | 170 | |
| 130 |
| Embodied Water, L/kg | 140 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 25 to 63 | |
| 22 |
| Strength to Weight: Bending, points | 21 to 39 | |
| 20 |
| Thermal Shock Resistance, points | 26 to 66 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0.75 to 0.85 | |
| 0 to 0.030 |
| Chromium (Cr), % | 3.8 to 5.0 | |
| 23 to 26 |
| Cobalt (Co), % | 7.0 to 9.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 1.2 |
| Iron (Fe), % | 60.6 to 68.3 | |
| 6.0 to 24 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.5 to 1.3 | |
| 6.0 to 9.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 47 to 52 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.4 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0 to 0.69 |
| Tungsten (W), % | 17.5 to 19 | |
| 0 to 3.0 |
| Vanadium (V), % | 1.8 to 2.4 | |
| 0 |