SiAlON vs. Lithium Fluoride
SiAlON belongs to the non-oxide engineering ceramics classification, while lithium fluoride belongs to the non-glass optical ceramics. There are 11 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is SiAlON and the bottom bar is lithium fluoride.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 290 | |
| 120 |
| Poisson's Ratio | 0.23 | |
| 0.27 |
| Shear Modulus, GPa | 120 | |
| 52 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 880 | |
| 1560 |
| Thermal Conductivity, W/m-K | 19 | |
| 12 |
| Thermal Expansion, µm/m-K | 3.6 | |
| 32 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 9.3 | |
| 9.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.3 | |
| 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 50 | |
| 24 |
| Stiffness to Weight: Bending, points | 67 | |
| 62 |
| Thermal Diffusivity, mm2/s | 6.4 | |
| 2.9 |