Silicon Carbide vs. C-310 Titania-based Ceramic
Silicon carbide belongs to the non-oxide engineering ceramics classification, while C-310 titania-based ceramic belongs to the oxide-based engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is silicon carbide and the bottom bar is C-310 titania-based ceramic.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.0 to 3.2 | |
| 3.7 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 0.94 to 3.3 | |
| 10 |
| Flexural Strength, MPa | 410 to 600 | |
| 75 |
| Specific Heat Capacity, J/kg-K | 670 to 1180 | |
| 750 |
| Thermal Conductivity, W/m-K | 120 to 170 | |
| 3.5 |
| Thermal Diffusivity, mm2/s | 38 to 79 | |
| 1.3 |
| Thermal Expansion, µm/m-K | 4.0 to 4.5 | |
| 7.0 |