Silver Chloride vs. Lithium Fluoride

Both silver chloride and lithium fluoride are non-glass optical ceramics. There are 14 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is silver chloride and the bottom bar is lithium fluoride.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 20
120
Poisson's Ratio 0.4
0.27
Shear Modulus, GPa 7.0
52

Thermal Properties

Melting Onset (Solidus), °C 460
870
Specific Heat Capacity, J/kg-K 360
1560
Thermal Conductivity, W/m-K 1.2
12
Thermal Expansion, µm/m-K 31
32

Electrical Properties

Dielectric Constant (Relative Permittivity) At 1 MHz 12
9.0

Otherwise Unclassified Properties

Density, g/cm3 5.6
2.6
Light Transmission Range, µm 0.4 to 25
0.12 to 6.5
Refractive Index 2.0
1.4

Common Calculations

Stiffness to Weight: Axial, points 2.0
24
Stiffness to Weight: Bending, points 16
62
Thermal Diffusivity, mm2/s 0.57
2.9