Soda-lime Glass vs. 8176 Aluminum
Soda-lime glass and 8176 aluminum belong to fundamentally different material chemistries. Soda-lime glass is a ceramic material, while 8176 aluminum is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is soda-lime glass and the bottom bar is 8176 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 70 to 71 | |
69 |
Poisson's Ratio | 0.23 | |
0.33 |
Shear Modulus, GPa | 29 | |
26 |
Tensile Strength: Ultimate (UTS), MPa | 41 to 180 | |
160 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 300 | |
170 |
Specific Heat Capacity, J/kg-K | 720 to 800 | |
900 |
Thermal Conductivity, W/m-K | 1.0 to 1.1 | |
230 |
Thermal Expansion, µm/m-K | 8.8 to 9.0 | |
24 |
Otherwise Unclassified Properties
Density, g/cm3 | 2.4 | |
2.7 |
Common Calculations
Stiffness to Weight: Axial, points | 16 | |
14 |
Stiffness to Weight: Bending, points | 56 | |
50 |
Strength to Weight: Axial, points | 4.6 to 20 | |
16 |
Strength to Weight: Bending, points | 11 to 28 | |
24 |
Thermal Diffusivity, mm2/s | 0.51 to 0.6 | |
93 |
Thermal Shock Resistance, points | 4.7 to 20 | |
7.0 |