Soda-lime Glass vs. C71000 Copper-nickel

Soda-lime glass and C71000 copper-nickel belong to fundamentally different material chemistries. Soda-lime glass is a ceramic material, while C71000 copper-nickel is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is soda-lime glass and the bottom bar is C71000 copper-nickel.

Soda-Lime (Float) GlassUNS C71000 Copper-Nickel
Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70 to 71
130
Poisson's Ratio 0.23
0.33
Shear Modulus, GPa 29
49
Tensile Strength: Ultimate (UTS), MPa 41 to 180
320 to 560

Thermal Properties

Maximum Temperature: Mechanical, °C 300
240
Specific Heat Capacity, J/kg-K 720 to 800
400
Thermal Conductivity, W/m-K 1.0 to 1.1
43
Thermal Expansion, µm/m-K 8.8 to 9.0
15

Otherwise Unclassified Properties

Density, g/cm3 2.4
8.9

Common Calculations

Stiffness to Weight: Axial, points 16
8.2
Stiffness to Weight: Bending, points 56
19
Strength to Weight: Axial, points 4.6 to 20
10 to 18
Strength to Weight: Bending, points 11 to 28
12 to 17
Thermal Diffusivity, mm2/s 0.51 to 0.6
12
Thermal Shock Resistance, points 4.7 to 20
12 to 20