Soda-lime Glass vs. C75700 Nickel Silver

Soda-lime glass and C75700 nickel silver belong to fundamentally different material chemistries. Soda-lime glass is a ceramic material, while C75700 nickel silver is a metal. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is soda-lime glass and the bottom bar is C75700 nickel silver.

Soda-Lime (Float) GlassUNS C75700 (CW403J) Nickel Silver
Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70 to 71
120
Poisson's Ratio 0.23
0.32
Shear Modulus, GPa 29
45
Tensile Strength: Ultimate (UTS), MPa 41 to 180
590 to 610

Thermal Properties

Maximum Temperature: Mechanical, °C 300
180
Specific Heat Capacity, J/kg-K 720 to 800
390
Thermal Conductivity, W/m-K 1.0 to 1.1
40
Thermal Expansion, µm/m-K 8.8 to 9.0
16

Otherwise Unclassified Properties

Density, g/cm3 2.4
8.4

Common Calculations

Stiffness to Weight: Axial, points 16
7.8
Stiffness to Weight: Bending, points 56
19
Strength to Weight: Axial, points 4.6 to 20
19 to 20
Strength to Weight: Bending, points 11 to 28
19
Thermal Diffusivity, mm2/s 0.51 to 0.6
12
Thermal Shock Resistance, points 4.7 to 20
22 to 23