Steatite vs. Lithium Fluoride
Steatite belongs to the oxide-based engineering ceramics classification, while lithium fluoride belongs to the non-glass optical ceramics. There are 11 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is steatite and the bottom bar is lithium fluoride.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 to 120 | |
| 120 |
| Poisson's Ratio | 0.23 | |
| 0.27 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 850 to 860 | |
| 1560 |
| Thermal Conductivity, W/m-K | 1.8 to 2.5 | |
| 12 |
| Thermal Expansion, µm/m-K | 7.0 to 9.0 | |
| 32 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 5.7 to 6.5 | |
| 9.0 |
| Electrical Dissipation At 1 MHz | 0.0010 to 0.0060 | |
| 0.00020 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.9 to 2.8 | |
| 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 to 32 | |
| 24 |
| Stiffness to Weight: Bending, points | 52 to 83 | |
| 62 |
| Thermal Diffusivity, mm2/s | 0.79 to 1.1 | |
| 2.9 |