Steatite vs. C-310 Titania-based Ceramic
Both steatite and C-310 titania-based ceramic are oxide-based engineering ceramics. There are 11 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is steatite and the bottom bar is C-310 titania-based ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Flexural Strength, MPa | 32 to 150 | |
| 75 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 850 to 860 | |
| 750 |
| Thermal Conductivity, W/m-K | 1.8 to 2.5 | |
| 3.5 |
| Thermal Expansion, µm/m-K | 7.0 to 9.0 | |
| 7.0 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 6.0 | |
| 70 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.9 to 16 | |
| 9.0 |
| Electrical Dissipation At 1 Hz | 0.0014 to 0.022 | |
| 0.0056 |
| Electrical Dissipation At 1 MHz | 0.0010 to 0.0060 | |
| 0.0018 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 8.0 to 11 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.9 to 2.8 | |
| 3.7 |
Common Calculations
| Thermal Diffusivity, mm2/s | 0.79 to 1.1 | |
| 1.3 |