Thallium Bromoiodide vs. Lead-alkali-silica Glass

Thallium bromoiodide belongs to the non-glass optical ceramics classification, while lead-alkali-silica glass belongs to the glass and glass-ceramics. There are 5 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is thallium bromoiodide and the bottom bar is lead-alkali-silica glass.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 7.4
3.1
Elastic (Young's, Tensile) Modulus, GPa 31
67
Stiffness to Weight: Axial, points 2.3
12
Stiffness to Weight: Bending, points 14
43
Thermal Expansion, µm/m-K 6.0
9.0