C-310 Titania-based Ceramic vs. Boron Carbide
C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while boron carbide belongs to the non-oxide engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is boron carbide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 2.1 to 2.7 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 0 to 11 |
| Flexural Strength, MPa | 75 | |
| 170 to 410 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 950 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 31 to 90 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 16 to 38 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 4.5 to 5.6 |