C-310 Titania-based Ceramic vs. Cordierite

Both C-310 titania-based ceramic and cordierite are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is cordierite.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 3.7
2.0 to 2.2
Dielectric Strength (Breakdown Potential), kV/mm 9.0
Electrical Resistivity Order of Magnitude, 10x Ω-m 10
Flexural Strength, MPa 75
17 to 32
Specific Heat Capacity, J/kg-K 750
800 to 850
Thermal Conductivity, W/m-K 3.5
1.3 to 1.7
Thermal Diffusivity, mm2/s 1.3
0.74 to 1.0
Thermal Expansion, µm/m-K 7.0
2.9 to 4.8