C-310 Titania-based Ceramic vs. Forsterite
Both C-310 titania-based ceramic and forsterite are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is forsterite.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 2.1 to 3.1 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.0 | |
| 7.9 |
| Electrical Dissipation At 1 MHz | 0.0018 | |
| 0.00030 |
| Flexural Strength, MPa | 75 | |
| 40 to 160 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 850 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 1.7 to 3.5 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 0.94 to 1.3 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 9.0 to 10 |