C-310 Titania-based Ceramic vs. Glass-bonded Mica
C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while glass-bonded mica belongs to the glass and glass-ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is glass-bonded mica.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 2.6 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.0 | |
| 20 |
| Electrical Dissipation At 1 MHz | 0.0018 | |
| 0.0016 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 10 |
| Flexural Strength, MPa | 75 | |
| 79 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 500 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 23 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 18 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 6.7 |