C-310 Titania-based Ceramic vs. Grade A Lava
Both C-310 titania-based ceramic and grade A lava are oxide-based engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is grade A lava.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 2.3 to 2.5 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.0 | |
| 3.2 to 3.9 |
| Flexural Strength, MPa | 75 | |
| 28 to 69 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 840 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 2.0 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 1.0 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 2.5 to 3.3 |