C-310 Titania-based Ceramic vs. Lithium Fluoride
C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while lithium fluoride belongs to the non-glass optical ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is lithium fluoride.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 2.6 |
| Electrical Dissipation At 1 MHz | 0.0018 | |
| 0.00020 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 1560 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 12 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 2.9 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 32 |