C-310 Titania-based Ceramic vs. Magnesium Fluoride
C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while magnesium fluoride belongs to the non-glass optical ceramics. There are 5 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is magnesium fluoride.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 3.2 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 980 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 28 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 8.8 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 11 |