C-310 Titania-based Ceramic vs. Magnesium Titanate
Both C-310 titania-based ceramic and magnesium titanate are oxide-based engineering ceramics.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is magnesium titanate.
Metric UnitsUS Customary Units
Mechanical Properties
| Flexural Strength, MPa | 75 | |
| 80 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 750 | |
| 950 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 3.8 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 8.0 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 70 | |
| 26 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.0 | |
| 9.1 |
| Electrical Dissipation At 1 Hz | 0.0056 | |
| 0.0017 |
| Electrical Dissipation At 1 MHz | 0.0018 | |
| 0.0013 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 9.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.7 | |
| 3.5 |
Common Calculations
| Thermal Diffusivity, mm2/s | 1.3 | |
| 1.1 |