C-310 Titania-based Ceramic vs. SiAlON
C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while SiAlON belongs to the non-oxide engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is SiAlON.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 3.3 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.0 | |
| 8.3 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 14 |
| Flexural Strength, MPa | 75 | |
| 680 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 880 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 19 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 6.4 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 3.6 |