C-310 Titania-based Ceramic vs. Silicon Carbide
C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while silicon carbide belongs to the non-oxide engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is silicon carbide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.7 | |
| 3.0 to 3.2 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 | |
| 0.94 to 3.3 |
| Flexural Strength, MPa | 75 | |
| 410 to 600 |
| Specific Heat Capacity, J/kg-K | 750 | |
| 670 to 1180 |
| Thermal Conductivity, W/m-K | 3.5 | |
| 120 to 170 |
| Thermal Diffusivity, mm2/s | 1.3 | |
| 38 to 79 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 4.0 to 4.5 |