C-310 Titania-based Ceramic vs. Tungsten Carbide

C-310 titania-based ceramic belongs to the oxide-based engineering ceramics classification, while tungsten carbide belongs to the non-oxide engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C-310 titania-based ceramic and the bottom bar is tungsten carbide.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 3.7
15
Electrical Resistivity Order of Magnitude, 10x Ω-m 10
0.75
Flexural Strength, MPa 75
1830
Specific Heat Capacity, J/kg-K 750
280
Thermal Conductivity, W/m-K 3.5
85
Thermal Diffusivity, mm2/s 1.3
21
Thermal Expansion, µm/m-K 7.0
5.4