Titanium 15-3-3-3 vs. EN 1.3961 Alloy
Titanium 15-3-3-3 belongs to the titanium alloys classification, while EN 1.3961 alloy belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is titanium 15-3-3-3 and the bottom bar is EN 1.3961 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 5.7 to 8.0 | |
| 31 |
| Poisson's Ratio | 0.33 | |
| 0.3 |
| Shear Modulus, GPa | 39 | |
| 72 |
| Shear Strength, MPa | 660 to 810 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 1120 to 1390 | |
| 450 |
| Tensile Strength: Yield (Proof), MPa | 1100 to 1340 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 270 |
| Melting Completion (Liquidus), °C | 1620 | |
| 1430 |
| Melting Onset (Solidus), °C | 1560 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 460 |
| Thermal Expansion, µm/m-K | 9.8 | |
| 1.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 40 | |
| 25 |
| Density, g/cm3 | 4.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 59 | |
| 4.8 |
| Embodied Energy, MJ/kg | 950 | |
| 66 |
| Embodied Water, L/kg | 260 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 89 | |
| 130 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 32 | |
| 23 |
| Strength to Weight: Axial, points | 64 to 80 | |
| 15 |
| Strength to Weight: Bending, points | 50 to 57 | |
| 16 |
| Thermal Shock Resistance, points | 79 to 98 | |
| 130 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.050 |
| Chromium (Cr), % | 2.5 to 3.5 | |
| 0 to 0.25 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 60.7 to 65 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 35 to 37 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 2.5 to 3.5 | |
| 0 |
| Titanium (Ti), % | 72.6 to 78.5 | |
| 0 |
| Vanadium (V), % | 14 to 16 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |