Titanium 15-3-3-3 vs. C82600 Copper
Titanium 15-3-3-3 belongs to the titanium alloys classification, while C82600 copper belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is titanium 15-3-3-3 and the bottom bar is C82600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 5.7 to 8.0 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 39 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 1120 to 1390 | |
| 570 to 1140 |
| Tensile Strength: Yield (Proof), MPa | 1100 to 1340 | |
| 320 to 1070 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 300 |
| Melting Completion (Liquidus), °C | 1620 | |
| 950 |
| Melting Onset (Solidus), °C | 1560 | |
| 860 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 390 |
| Thermal Conductivity, W/m-K | 8.1 | |
| 130 |
| Thermal Expansion, µm/m-K | 9.8 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.2 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.3 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 59 | |
| 11 |
| Embodied Energy, MJ/kg | 950 | |
| 180 |
| Embodied Water, L/kg | 260 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 89 | |
| 11 to 97 |
| Stiffness to Weight: Axial, points | 12 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 32 | |
| 19 |
| Strength to Weight: Axial, points | 64 to 80 | |
| 18 to 36 |
| Strength to Weight: Bending, points | 50 to 57 | |
| 17 to 28 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 37 |
| Thermal Shock Resistance, points | 79 to 98 | |
| 19 to 39 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.5 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 2.3 to 2.6 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 2.5 to 3.5 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.35 to 0.65 |
| Copper (Cu), % | 0 | |
| 94.9 to 97.2 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.13 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.35 |
| Tin (Sn), % | 2.5 to 3.5 | |
| 0 to 0.1 |
| Titanium (Ti), % | 72.6 to 78.5 | |
| 0 to 0.12 |
| Vanadium (V), % | 14 to 16 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |