Titanium 4-4-2 vs. SAE-AISI 1018 Steel
Titanium 4-4-2 belongs to the titanium alloys classification, while SAE-AISI 1018 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is titanium 4-4-2 and the bottom bar is SAE-AISI 1018 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 10 | |
| 17 to 27 |
| Fatigue Strength, MPa | 590 to 620 | |
| 180 to 270 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Reduction in Area, % | 20 | |
| 45 to 57 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Shear Strength, MPa | 690 to 750 | |
| 280 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 1150 to 1250 | |
| 430 to 480 |
| Tensile Strength: Yield (Proof), MPa | 1030 to 1080 | |
| 240 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 400 |
| Melting Completion (Liquidus), °C | 1610 | |
| 1460 |
| Melting Onset (Solidus), °C | 1560 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 470 |
| Thermal Conductivity, W/m-K | 6.7 | |
| 52 |
| Thermal Expansion, µm/m-K | 8.6 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 1.8 |
| Density, g/cm3 | 4.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 30 | |
| 1.4 |
| Embodied Energy, MJ/kg | 480 | |
| 18 |
| Embodied Water, L/kg | 180 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 75 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 4700 to 5160 | |
| 150 to 430 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 34 | |
| 24 |
| Strength to Weight: Axial, points | 68 to 74 | |
| 15 to 17 |
| Strength to Weight: Bending, points | 52 to 55 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 14 |
| Thermal Shock Resistance, points | 86 to 93 | |
| 14 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 3.0 to 5.0 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0.15 to 0.2 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 98.8 to 99.25 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 3.0 to 5.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.3 to 0.7 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 |
| Titanium (Ti), % | 85.8 to 92.2 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |